THERMOLAST® K CS Series | TPE Thermoplastic Elastomer |
![]() |
Processing Method:
Injection Molding, Extrusion
Color / RAL DESIGN: Natural / Black
|
Availability:
Globally
Premium Quality Thermoplastic Elastomer TPE Granules TPE Resin
|
Typical applications
|
Material features
|
MODEL | COLOR / RAL DESINE | Hardness DIN ISO 7619-1 Shore A |
Density DIN EN ISO 1183-1 g/3cm |
Tensile Strength 1 DIN 53504/ISO 37 MPa |
Elongation at Break1 DIN 53504/ISO 37 % |
Tear Strength ISO 34-1 Method B (b)(Graves) N/mm |
CS 72h/23 °C DIN ISO 815-1 Method A % |
CS 24h/70 °C DIN ISO 815-1 Method A % |
CS 24h/100 °C DIN ISO 815-1 Method A % |
CS 24h/120 °C DIN ISO 815-1 Method A % |
TC3CSN | Natural | 27 | 1.100 | 4.0 | 550 | 12.0 | 14 | 18 | 33 | 58 |
TC3CSZ | Black | 30 | 1.100 | 3.5 | 550 | 8.0 | 16 | 20 | 33 | 55 |
TC4CSN | Natural | 38 | 1.100 | 5.0 | 550 | 10.0 | 13 | 19 | 35 | 58 |
TC4CSZ | Black | 37 | 1.100 | 4.0 | 550 | 12.5 | 15 | 19 | 35 | 58 |
TC5CSN | Natural | 46 | 1.100 | 7.0 | 550 | 12.0 | 19 | 20 | 35 | 57 |
TC5CSZ | Black | 50 | 1.100 | 6.0 | 500 | 12.0 | 19 | 21 | 35 | 56 |
TC6CSN | Natural | 56 | 1.100 | 8.0 | 600 | 17.0 | 20 | 22 | 40 | 60 |
TC6CSZ | Black | 58 | 1.100 | 7.0 | 500 | 15.0 | 20 | 22 | 37 | 60 |
TC7CSN | Natural | 68 | 1.100 | 8.0 | 500 | 21.0 | 23 | 33 | 46 | 72 |
TC7CSZ | Black | 69 | 1.100 | 8.0 | 500 | 20.0 | 23 | 30 | 46 | 72 |
TC8CSN | Natural | 79 | 1.100 | 9.0 | 500 | 26.5 | 30 | 42 | 55 | 75 |
TC8CSZ | Black | 78 | 1.100 | 9.0 | 500 | 25.0 | 30 | 33 | 54 | 75 |
TC9CSN | Natural | 86 | 1.100 | 10.0 | 500 | 31.0 | 36 | 45 | 63 | 82 |
TC9CSZ | Black | 87 | 1.100 | 10.0 | 500 | 34.0 | 36 | 45 | 63 | 82 |
Cylinder Temperature | 180 - 200 - 220 °C, max. 250 °C (360 - 390 - 430 °F, max. 480 °F) |
Hotrunner | Hot runner temperatures: 200 -250 °C (390 - 480 °F). The runner should be empty after a maximum of 2 - 3 shots. |
Injection Pressure | 200 - 1000 bar (2900 - 14504 psi) (depending on the size and weight of the part). |
Injection Rate | In general, the fill time should not be more than 1-2 seconds. |
Hold Pressure | We recommend to derive the optimum hold pressure from determining the solidification point, starting with 40 % - 60 % of the required injection pressure. |
Back Pressure | 20 - 100 bar; if color batches are used, higher back pressure is necessary. |
Screw Retraction | If an open nozzle is used processing with screw retraction is advisable. |
Mold Temperature | 25 - 40 °C (77 - 104 °F) |
Predrying | Pre drying of the material is not necessary; if surface moisture forms as a result of changes in temperature, the material should be dried for 2 - 4 hours at 60 - 80 °C (140 - 175 °F). |
Needle Valve | With materials < 50 Shore A the use of a needle valve is advisable. |
Screw Geometry | Standard 3-zone polyolefine screw. |
Residence Time | The residence time is to be set as short as possible with a maximum of 10 minutes. |
Cleaning Recommendation | For cleaning and purging of the machine it is appropriate to use polypropylene or polyethylene. Machine must be PVC-free. |
Cylinder Temperature | 160 - 180 - 200 °C, max. 250 °C (320 - 360 - 390 °F; max. 480 °F) |
Screw Geometry | Standard three-zone screw (e.g. polyolefin screw). The screw must be able to provide sufficient shearing. |
L/D Ratio | At least 25 |
Compression Ratio | At least 3.5 : 1 |
Screens / Breaker Plate | A breaker plate and a screen pack are generally recommended in the extruder configuration in order to increase pressure. |
Die Land | <= 3 mm ( <= 0,12 in.) |
Extruder Head | Ca. 200 °C (390 °F) |
Die Temperature | Ca. 200 - 230 °C (390 - 450 °F) |
Predrying | Pre drying of the material is not necessary; if surface moisture forms as a result of changes in temperature, the material should be dried for 2 - 4 hours at 60 - 80 °C (140 - 175 °F). To avoid porosity in the profile a pre drying is recommended for wall thickness > 3mm. |
Calibration | Generally not necessary; support elements may be required when extruding THERMOLAST® compounds with high hardness or when coextruding with standard thermoplastics. |
Cleaning Recommendation | For cleaning and purging of the machine it is appropriate to use polypropylene or polyethylene. Machine must be PVC-free. |