Customization: | Available |
---|---|
Color: | White |
Usage: | Engineering Plastics |
Still deciding? Get samples of US$ 0.1/kg
Order Sample
|
Shipping Cost: | Contact the supplier about freight and estimated delivery time. |
---|
Payment Methods: |
|
---|---|
Support payments in USD |
Secure payments: | Every payment you make on Made-in-China.com is protected by the platform. |
---|
Refund policy: | Claim a refund if your order doesn't ship, is missing, or arrives with product issues. |
---|
Suppliers with verified business licenses
Audited by an independent third-party inspection agency
DuPont Performance Polymers Zytel® 101L BKB080 Nylon 66 (Unverified Data**) Nylon 66
Physical properties | Rating | Rating | test method |
density | 1.14 g/cc | 0.0412 lb/in³ | DAM; ISO 1183 |
mechanical properties | Rating | Rating | test method |
55.0 MPa | 7980 psi | ||
()Tensile strength (yield | @Temperature 23.0 °C | @Temperature 73.4 °F | 50%RH; ISO 527 |
82.0 MPa | 11900 psi | ||
@Temperature 23.0 °C | @Temperature 73.4 °F | DAM; ISO 527 | |
25 % | 25 % | ||
()Elongation (broken) | @Temperature 23.0 °C | @Temperature 73.4 °F | DAM; nominal; ISO 527 |
45 % | 45 % | ||
@Temperature 23.0 °C | @Temperature 73.4 °F | 50mm/min; DAM; ISO 527 | |
>= 50 % | >= 50 % | ||
@Temperature 23.0 °C | @Temperature 73.4 °F | 50%RH; nominal; ISO 527 | |
4.3 % | 4.3 % | ||
Elongation at Yield | @Temperature 23.0 °C | @Temperature 73.4 °F | DAM; ISO 527 |
25 % | 25 % | ||
@Temperature 23.0 °C | @Temperature 73.4 °F | 50%RH; ISO 527 | |
1.40 GPa | 203 ksi | ||
Tensile modulus | @Temperature 23.0 °C | @Temperature 73.4 °F | 50%RH; ISO 527 |
3.10 GPa | 450 ksi | ||
@Temperature 23.0 °C | @Temperature 73.4 °F | DAM; ISO 527 | |
2.80 GPa | 406 ksi | ||
Bending modulus | @Temperature 23.0 °C | @Temperature 73.4 °F | DAM; ISO 178 |
5.50 kJ/m² | 2.62 ft-lb/in² | ||
Notched impact strength of overhanging beam | @Temperature 23.0 °C | @Temperature 73.4 °F | DAM; ISO 180/1A |
NB | NB | ||
Cantilever beam has no notched impact strength | @Temperature 23.0 °C | @Temperature 73.4 °F | DAM; ISO 180/1U |
NB | NB | ||
Simply supported beams have no notched impact strength | @Temperature 23.0 °C | @Temperature 73.4 °F | DAM; ISO 179/1eU |
0.550 J/cm² | 2.62 ft-lb/in² | ||
Notched impact strength of simple supported beam | @Temperature 23.0 °C | @Temperature 73.4 °F | DAM; ISO 179/1eA |
Thermal performance | Rating | Rating | test method |
(0.46 MPa)Thermal deformation temperature under load | 200 °C | 392 °F | DAM; ISO 75-1/-2 |
(1.8 MPa)Thermal deformation temperature under load | 70.0 °C | 158 °F | DAM; ISO 75-1/-2 |
UL RTI |
130 °C @Thickness 0.710 mm |
266 °F @Thickness 0.0280 in |
DAM; UL 746B |
75.0 °C | 167 °F | ||
UL RTI,Mechanical impact | @Thickness 0.710 mm | @Thickness 0.0280 in | DAM; UL 746B |
85.0 °C | 185 °F | ||
UL RTI,Mechanical shock free | @Thickness 0.710 mm | @Thickness 0.0280 in | DAM; UL 746B |
(UL94) |
V-2 @Thickness 0.710 mm |
V-2 @Thickness 0.0280 in |
DAM; IEC 60695-11-10 |
V-2 | V-2 | ||
@Thickness 0.710 mm | @Thickness 0.0280 in | DAM; UL94 |
960 °C @Thickness 3.00 mm |
1760 °F @Thickness 0.118 in |
DAM; IEC 60695-2-12 |
|
960 °C | 1760 °F | ||
@Thickness 1.50 mm | @Thickness 0.0591 in | DAM; IEC 60695-2-12 | |
960 °C | 1760 °F | ||
@Thickness 0.710 mm | @Thickness 0.0280 in | DAM; IEC 60695-2-12 | |
processability | Rating | Rating | test method |
()Processing melt temperature | 290 °C | 554 °F | DAM; Optimum |
280 - 300 °C | 536 - 572 °F | DAM | |
Mold temperature | 70.0 °C | 158 °F | DAM; optimum |
50.0 - 90.0 °C | 122 - 194 °F | DAM | |
Drying temperature | 80.0 °C | 176 °F | DAM |
Drying time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM |
Moisture content | < = 0.20 % | < = 0.20 % | DAM |
Material description | test method | ||
appearance | Black Color | DAM | |
peculiarity | Chemical Resistance, Good | DAM | |
Cycle (Production), Fast | DAM | ||
Electrical Properties, Good | DAM | ||
Fatigue Resistant | DAM | ||
Flow, High | DAM | ||
Fuel Resistant | DAM | ||
Grease Resistant | DAM | ||
Lubricated | DAM | ||
Mold Release, Good | DAM | ||
Moldability, Good | DAM | ||
Molecular Wt., Low | DAM | ||
Oil Resistant | DAM | ||
Processability, Good | DAM | ||
Wear Resistance, Good | DAM | ||
form | Pellets | DAM | |
Generic | Nylon 66 | DAM | |
Material Status | Current | DAM | |
Part identification code | >PA66< | ISO 11469; DAM | |
Processing method | Injection Molding | DAM |
COMPANY INFORMATION
|
|
Our company is a plastic manufacturer and agent for internationally renowned brands: 1. Kunshan Lizhao Plastic Co., Ltd. Was established in 2009 with a registered capital of 21.24 million yuan and an area of 20, 000 square meters. Our company has 14 high-speed production lines and 3 R&D experimental production lines, with a monthly production capacity of 3, 500 tons. Our company specializes in R&D and production of PP PBT PA6 PA66 PPA PC PC/ABS. The company has first-class production equipment and is equipped with professional product laboratories, testing rooms, and sample warehouses. We always adhere to the principle of "quality first" and strive for perfection. Our company has IS09001: 2008 quality system certification and ISO/TS16949-2009 automotive quality system certification. The company starts from selecting the best raw materials and standardizes, processes and institutionalizes product processing. 2. Suzhou Furenxiang Trading Co., Ltd. Was established in 2016 and is committed to the import and export of our own materials and internationally renowned brand materials. Sales brands include: DuPont, Covestro, Polytechnic, Toray, Asahi Kasei, Teijin, LG EMS. Model types include: PP PC PC/ABS ABS PPO PBT POM PA6 PA66 PPA LCP TPE TPU ASA PCR (PC/ABS PC/PET), etc. |